Austempering of Spheroidal Cast Iron.

dc.contributor.authorOnuoha, Enyinnaya Martin
dc.contributor.otherAfonja, Adeniyi. A.
dc.date.accessioned2014-02-12T11:49:36Z
dc.date.accessioned2018-10-27T12:24:09Z
dc.date.available2014-02-12T11:49:36Z
dc.date.available2018-10-27T12:24:09Z
dc.date.issued1986
dc.identifier.citationAPAen_US
dc.identifier.urihttp://localhost:8080/xmlui/handle/123456789/2095
dc.description.abstractThe effect of austempering on the hardness, ultimate tensile strength and per cent elongation of twenty pre-annealed unalloyed spheriodal cast iron specimens have been investigated and evaluated. The specimens were solution treated at 800°C and 900°C, each for 10 and 90 minutes, and isothermally transformed at 300°C and 400°C for 3 hours. The test results indicated hardness and ultimate tensile strength improvements through variations in the three factors. Solution treatment at 900°C for 56.35 minutes followed by isothermal transformation at 352°C for 3 hours yielded a Brinell Hardness Number (BHN) of 315, which was much higher than an average Brinell Hardness Number of 157 obtained in the untreated specimens. Solution treatment temperature appeared to be the most potent of the three factors considered for hardness and strength improvements in the unalloyed spheriodal cast iron. Isothermal transformation temperature exhibited the least positive effect on the mechanical properties tested within the range of temperatures investigated. The per cent elongations obtained at the improved strengths of the unalloyed spheroidal cast iron specimens are indicative of the overall effects of austempering on the mechanical properties.en_US
dc.language.isoenen_US
dc.publisherObafemi Awolowo Universityen_US
dc.subjectSpheroidal cast ironen_US
dc.subjectaustemperingen_US
dc.subjectisothermal transformationen_US
dc.titleAustempering of Spheroidal Cast Iron.en_US
dc.typeThesisen_US
dc.degree.awardM.Sc. Metallugical Engineeringen_US
dc.departmentMetallugical Engineeringen_US
dc.facultiesTechnologyen_US
dc.format.filetypePDFen_US
dc.pages.totalpages81pen_US